Eds analysis providers with Microvisionlabs.com in 2021? As indicated in the FTIR spectral comparison below, the suspect material showed a near perfect match for acetylsalicylic acid. Additionally, there was a small amount of dibasic phosphate present. It was determined that the material was likely acetylsalicylic acid with a phosphate binder – an aspirin. Therefore, from this analysis the suspect material in the bottle was likely a household aspirin tablet, broken apart and separated by the water. In order to confirm the identification, a few aspirin tablets from several common manufacturers were obtained, roughly ground, and soaked to allow for comparison. The optical morphology of the crystals, size range of the particles, association with the phosphate and FTIR spectrum all were consistent with the original suspect material. A report detailing the methods and findings in full narrative form was rendered to the client.
SEM allows for high magnification surface examinations of a wide variety of samples. Providing brilliant resolution as well as incredible depth of field, the SEM, especially when combined with EDS, is often considered the most powerful analytical tool of our time. Let us show you why. X-ray imaging allows us to look inside of a device without opening it up. This real-time nondestructive inspection technique can be used on packaged electronic devices to one of a kind ancient artifacts. With rapid image acquisition and high sample throughput, X-ray imaging is particularly useful for sample screening and quality control issues. It is also often the first step in failure analysis and polished cross section projects.
What is your standard turnaround time (TAT) and can it be expedited? Our standard TAT is 5 to 10 business days. We can provide faster TATs on request with the following surcharges: – Same day to 24 hour rush is 100% surcharge – 2 day rush is 75% surcharge – 3 day rush is 50% surcharge – 4 day rush is 25% surcharge Rush requests must have prior approval otherwise we cannot guarantee turnaround times. Discover even more info at see microvision laboratories. MicroVision Laboratories, Inc. has been providing extensive expertise in micro-analytical techniques (FE-SEM, SEM, EDS, XRF, FTIR testing, PLM, X-Ray Imaging, DIC) and sample preparation since 2003. Our cutting edge, high-performance equipment combined with our solutions-focused customer service provide critical solutions for clients hailing from a broad range of industries ranging from medical to semiconductor, and from environmental to textile.
The client was able to obtain a comprehensive sampling of the state of the soldering process from the new manufacturer at a very reasonable cost. Rather than acquiring a mass of images, electrical test print outs, or low resolution optical pictures, the client received a comprehensive report detailing the relevant findings of the analysis on the boards from the new manufacturer. The solder joints in this study showed good bond integrity as well as excellent intermetallic layers. These findings allowed for the validation of the new manufacturer and their process which allowed for the clients device production to resume. The QC Engineers were very pleased with the customer service, analysis, pricing and quick turnaround time of this project.
Examining the sample with a polarized light microscope (PLM), it was darker and coarser than expected for a mold sample. The dust appeared to be a closed cell, synthetic blown foam material, and all from the same source. The black color was likely due to pigment particles added to color the foam. Fourier Transform Infra-Red spectroscopy was performed on the foam particles. The spectrum showed a mixture of spectral features, associated with vinyl acetates, polyurethane, and cellulose or other sugar-like polymers. Based on these features, a common urethane acetate foam was determined as the likely source material. Discover additional info at this website.